HAYNES 188 alloy (UNS R30188) is a cobalt-nickel-chromium-tungsten alloy that combines excellent high-temperature strength with very good resistance to oxidizing environments up to 2000°F (1095°C) for prolonged exposures, and excellent resistance to sulfate deposit hot corrosion. It is readily fabricated and formed by conventional techniques, and has been used for cast component. Other attractive features include excellent resistance to molten chloride salts, and good resistance to gaseous sulfidation.
HAYNES 188 alloy has good forming and welding characteristics. It may be forged or other hot-worked, providing that it is held at 2150°F (1175°C) for a time sufficient to bring the entire piece to temperature. As a consequence of its good ductility, 188 alloy is also readily formed by cold working. The alloy does work-harden rapidly, however, so frequent intermediate annealing treatments may be needed for complex component forming operations. All hot- or cold- worked parts should be annealed and rapidly cooled in order to restore the best balance of properties.
The alloy can be welded by both manual and automatic welding methods, including gas tungsten arc (TIG), gas metal arc (MIG), electron beam and resistance welding. It exhibits good restraint welding characteristics.
Wrought HAYNES 188 alloy is furnished in the solution heat treated condition, unless otherwise specified. The alloy is normally solution heat-treated at 2125-2175°F (1163-1191°C) and rapidly cooled or water quenched for optimal properties.
Annealing at temperatures less than the solution heat-treating temperature will produce some carbide precipitation in alloy 188, which may affect the alloy’s properties.
Haynes 188 (UNS R30188 / W.Nr. 2.4683) is a cobalt-nickel-chromium-tungsten alloy that com- bines excellent high-temperature strength with very good resistance to oxidizing environ- ments up to 1095ºC for prolonged exposures, and excellent resistance to sulfate deposit hot corrosion. It is readily fabricated and formed by conventional techniques, and has been used for cast component. Other attractive features include excellent resistance to molten chloride salts, and good resistance to gaseous sulfidation.
| UNS | W. Nr | Trademark | GB | DIN | NF |
| R30188 | 2.4683 | Haynes 188 | GH5188 | KCN22W |
| Alloy | C | Si | Mn | P | S | Cr | Ni | Co | W | La | Fe |
| Haynes 188 | 0.05-0.15 | 0.2-0.5 | ≤1.25 | ≤0.02 | ≤0.015 | 20.0-24.0 | 20.0-24.0 | Bal | 13.0-15.0 | 0.03-0.15 | ≤3.0 |
| Density, g/cm3 | Melting Point, ºC | Tensile Strength, MPa | Yield Strength, MPa | ELongation, % | Hardness, HRB |
| 9.07 | 1330-1410 | 991 | 483 | 50.6 | / |
| Rod, Bar, Wire and Forgings | AMS 5772 |
| Plate, Sheet and Strip | AMS 5608 |
| Pipe and Tube | - |
| Welding Product | - |
| Others | - |
| Haynes 188 available sizes and specifications | |
| Grade | Haynes 188 |
| Nickel plate | Thickness: 0.3mm - 150.0mm
Width: 1000mm - 3000mm |
| Nickel strip/ nickel foil | Thickness: 0.02mm - 16.0mm Width: 5mm - 3000mm |
| Nickel coil | Thickness: 0.3mm - 16.0mm Width: 1000mm - 3000mm |
| Nickel pipe | Outside diameter: 6mm - 1219mm Thickness: 0.5mm - 100mm |
| Nickel Capillary Pipe | Outside diameter: 0.5mm - 6.0mm Thickness: 0.05mm - 2.0mm |
| Nickel bar | Diameter: Ф4mm - Ф600mm |
| Nickel wire rod | Diameter:Ф0.01mm - Ф6mm |
Q1: Do you accept the trial order ?
A1: Yes,if we have the exactly size in stock.we can delivery even 1 piece/meter .
Q2: Can I have free sample before making orders?
|
|
| MOQ: | 100 KGS |
| Preis: | USD28.5/KG |
| Standardverpackung: | Holzkisten |
| Lieferfrist: | 7 Tage |
| Zahlungsmethode: | L/C, T/T |
| Lieferkapazität: | 50000 KGS |
HAYNES 188 alloy (UNS R30188) is a cobalt-nickel-chromium-tungsten alloy that combines excellent high-temperature strength with very good resistance to oxidizing environments up to 2000°F (1095°C) for prolonged exposures, and excellent resistance to sulfate deposit hot corrosion. It is readily fabricated and formed by conventional techniques, and has been used for cast component. Other attractive features include excellent resistance to molten chloride salts, and good resistance to gaseous sulfidation.
HAYNES 188 alloy has good forming and welding characteristics. It may be forged or other hot-worked, providing that it is held at 2150°F (1175°C) for a time sufficient to bring the entire piece to temperature. As a consequence of its good ductility, 188 alloy is also readily formed by cold working. The alloy does work-harden rapidly, however, so frequent intermediate annealing treatments may be needed for complex component forming operations. All hot- or cold- worked parts should be annealed and rapidly cooled in order to restore the best balance of properties.
The alloy can be welded by both manual and automatic welding methods, including gas tungsten arc (TIG), gas metal arc (MIG), electron beam and resistance welding. It exhibits good restraint welding characteristics.
Wrought HAYNES 188 alloy is furnished in the solution heat treated condition, unless otherwise specified. The alloy is normally solution heat-treated at 2125-2175°F (1163-1191°C) and rapidly cooled or water quenched for optimal properties.
Annealing at temperatures less than the solution heat-treating temperature will produce some carbide precipitation in alloy 188, which may affect the alloy’s properties.
Haynes 188 (UNS R30188 / W.Nr. 2.4683) is a cobalt-nickel-chromium-tungsten alloy that com- bines excellent high-temperature strength with very good resistance to oxidizing environ- ments up to 1095ºC for prolonged exposures, and excellent resistance to sulfate deposit hot corrosion. It is readily fabricated and formed by conventional techniques, and has been used for cast component. Other attractive features include excellent resistance to molten chloride salts, and good resistance to gaseous sulfidation.
| UNS | W. Nr | Trademark | GB | DIN | NF |
| R30188 | 2.4683 | Haynes 188 | GH5188 | KCN22W |
| Alloy | C | Si | Mn | P | S | Cr | Ni | Co | W | La | Fe |
| Haynes 188 | 0.05-0.15 | 0.2-0.5 | ≤1.25 | ≤0.02 | ≤0.015 | 20.0-24.0 | 20.0-24.0 | Bal | 13.0-15.0 | 0.03-0.15 | ≤3.0 |
| Density, g/cm3 | Melting Point, ºC | Tensile Strength, MPa | Yield Strength, MPa | ELongation, % | Hardness, HRB |
| 9.07 | 1330-1410 | 991 | 483 | 50.6 | / |
| Rod, Bar, Wire and Forgings | AMS 5772 |
| Plate, Sheet and Strip | AMS 5608 |
| Pipe and Tube | - |
| Welding Product | - |
| Others | - |
| Haynes 188 available sizes and specifications | |
| Grade | Haynes 188 |
| Nickel plate | Thickness: 0.3mm - 150.0mm
Width: 1000mm - 3000mm |
| Nickel strip/ nickel foil | Thickness: 0.02mm - 16.0mm Width: 5mm - 3000mm |
| Nickel coil | Thickness: 0.3mm - 16.0mm Width: 1000mm - 3000mm |
| Nickel pipe | Outside diameter: 6mm - 1219mm Thickness: 0.5mm - 100mm |
| Nickel Capillary Pipe | Outside diameter: 0.5mm - 6.0mm Thickness: 0.05mm - 2.0mm |
| Nickel bar | Diameter: Ф4mm - Ф600mm |
| Nickel wire rod | Diameter:Ф0.01mm - Ф6mm |